>Wire rod for cold heading
Technological and metallurgical properties
Quenching hardenabilityBoron steels are killed with Aluminium and Titanium, which allow enough boron to be active in order to guarantee quenching hardenability of the steel.
Products are systematically checked according to the current standards of core hardness by quenching and JOMINY tests.
Surface qualityThe rod is rolled from 180 x 180 mm blooms of assured surface quality. Rolling process in strictly controled by computer for different parameters, allowing to get a product with a quality level which exceeds the requirements of EN 10221 Clase D.
Decarburization- Partial: Less than 1% of rod diameter.
- Free of total decarburization.
Standard chemical analysis and mechanical properties (II)
Geometrical characteristics
Range of diameters (mm)| 5,5 | 6 | 6,5 | 7 | 7,5 | 8 | 8,5 |
| 9 | 9,5 | 10 | 10,5 | 11 | 11,5 | 12 |
| 12,5 | 13 | 14 | 15 | 16 | 17 | 18 |
| 19 | 20 | 21 | 22 | 23 | 24 | - |
- 24 mm - 52 mm Garret Coils
Coils endsBoth ends are cold trimmed.
| Diameter mm | Standard tolerance | Special tolerance | Ovality |
|---|---|---|---|
| 5,5 - 10,0 | ± 0,20 | ± 0,15 | <=80% of tolerance |
| 10,5 - 15,0 | ± 0,25 | ± 0,20 | <=80% of tolerance |
| 16 - 26 | ± 0,30 | ± 0,25 | <=80% of tolerance |
| Coil Weight | 2600 kg. Upon request, 1500 kg | ||
| Coils dimensions | Outside diameter = 1210 mm Inside diameter = 900 mm Length = 1700 mm |
||
- As rolled (Stelmor cooling)
- Spheroidised annealed (*)
* Scale is removed by acid pickling before annealing
En caso de suministro de material recocido, el mismo se somete a decapado químico previo.
Surface conditionUpon request rod may be delivered with following surface conditions: Pickled.. phosfated.. limed Pickled.. phosfated.. soaped
| W.Nr | DIN Std Des. | Other Des. | EN 10263-2 Std Des. | GSW Des. | %C | %Mn | %Si | %P | %S | %Cr | %Al | Rmax N/mm2 |
Zmin (%) Red. in Area |
|---|---|---|---|---|---|---|---|---|---|---|---|---|---|
| 1.0303 | QST 32 - 3 | - | C4C | C05QAL | <= 0,06 | 0,25 - 0,40 | <= 0,10 | <= 0,020 | <= 0,020 | <= 0,15 | 0,020 - 0,060 | 390 | 70 |
| 1.0303 | QST 32 - 3 | - | C4C | C06QAL | <= 0,06 | 0,25 - 0,40 | <= 0,10 | <= 0,020 | <= 0,020 | <= 0,15 | 0,020 - 0,060 | - | - |
| 1.0213 | QST34 - 3 | - | C8C | C08QAL | 0,06 - 0,10 | 0,25 - 0,45 | <= 0,10 | <= 0,020 | <= 0,020 | <= 0,15 | 0,020 - 0,060 | 410 | 65 |
| 1.0214 | QST36 - 3 | - | C10C | C10QAL | 0,08 - 0,12 | 0,30 - 0,50 | <= 0,10 | <= 0,020 | <= 0,020 | <= 0,15 | 0,020 - 0,060 | 430 | 60 |
| 1.0214 | QST36 - 3 | - | C10C | C13QAL | 0,08 - 0,12 | 0,30 - 0,50 | <= 0,10 | <= 0,020 | <= 0,020 | <= 0,15 | 0,020 - 0,060 | - | - |
| 1.0234 | QST38 - 3 | CQ15 | C15C | C15QAL | 0,13 - 0,17 | 0,35 - 0,60 | <= 0,10 | <= 0,020 | <= 0,020 | <= 0,15 | 0,020 - 0,060 | 460 | 58 |
| 1.0234 | QST38 - 3 | CQ15 | C15C | C18QAL | 0,13 - 0,17 | 0,35 - 0,60 | <= 0,10 | <= 0,020 | <= 0,020 | <= 0,15 | 0,020 - 0,060 | - | - |
| 1.0434 | - | - | C17C | C19QAL | 0,15 - 0,19 | 0,65 - 0,85 | <= 0,10 | <= 0,020 | <= 0,020 | <= 0,15 | 0,020 - 0,060 | 520 | 58 |
| 1.0411 | - | CQ22 | C20C | C23QAL | 0,18 - 0,22 | 0,70 - 0,90 | <= 0,10 | <= 0,020 | <= 0,020 | <= 0,15 | 0,020 - 0,060 | 560 | 55 |
| GSW Standard specification. Individual variation in any element can be considered. | |||||||||||||
| W.Nr | DIN Std Des. | Other Des. | EN 10263 - 4:2002 Std Des. | GSW Des. | %C | %Mn | %Si | %P | %S | %Cr | %Al | B (ppm) | Rmax N/mm2 |
Zmin (%) Red. in Area |
|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|
| - | - | CQ15B | - | C15B | 0,14 - 0,18 | 0,60 - 0,90 | <= 0,15 | <= 0,020 | <= 0,020 | <= 0,30 | >= 0,020 | 10 - 50 | 500 | 450 |
| 1.5502 | - | - | 17B2 | C18B | 0,16 - 0,20 | 0,70 - 0,90 | <= 0,15 | <= 0,020 | <= 0,020 | <= 0,30 | >= 0,020 | 10 - 50 | 540 | 460 |
| 1.5506 | 17MNB | ASTM A320 | - | C18B | 0,06 - 0,20 | 0,70 - 0,90 | <= 0,15 | <= 0,020 | <= 0,020 | <= 0,30 | >= 0,020 | 10 - 50 | 540 | 460 |
| 1.5508 | 22B2 | ES F1291 | 23B2 | C22B | 0,19 - 0,25 | 0,60 - 0,80 | <= 0,15 | <= 0,020 | <= 0,020 | <= 0,30 | >= 0,020 | 10 - 50 | 600 | 490 |
| 1.5523 | 19MNB4 | ASTM A304 | 19MNB4 | C23B | 0,08 - 0,23 | 0,80 - 1,10 | <= 0,15 | <= 0,020 | <= 0,020 | <= 0,30 | >= 0,020 | 10 - 50 | 580 | 500 |
| 1.5525 | 20MNB4 | - | 20MNB4 | C23B1 | 0,18 - 0,23 | 0,90 - 1,20 | <= 0,15 | <= 0,020 | <= 0,020 | <= 0,30 | >= 0,020 | 10 - 50 | 590 | 510 |
| 1.5535 | - | - | 23MNB4 | C23BCR | 0,20 - 0,25 | 0,80 - 1,10 | <= 0,15 | <= 0,020 | <= 0,020 | 0,15 - 0,30 | >= 0,020 | 10 - 50 | 600 | 520 |
| 1.5530 | - | AF 20MB5 | 20MNB5 | C23B3 | 0,17 - 0,23 | 1,10 - 1,40 | <= 0,15 | <= 0,020 | <= 0,020 | <= 0,30 | >= 0,020 | 10 - 50 | 630 | 540 |
| 1.5530 | - | AF 20MNB5 | 20MNB5 | C23BCR3 | 0,17 - 0,23 | 1,10 - 1,40 | <= 0,15 | <= 0,020 | <= 0,020 | 0,10 - 0,30 | >= 0,020 | 10 - 50 | 650 | 550 |
| 1.5536 | - | - | 27MNB4 | C28B | 0,25 - <= 0,30 | 0,80 - 1,10 | <= 0,15 | <= 0,020 | <= 0,020 | <= 0,30 | >= 0,020 | 10 - 50 | 630 | 540 |
| 1.5510 | 28B2 | AF 25B3 | 28B2 | C28B | 0,25 - <= 0,30 | 0,60 - 0,90 | <= 0,15 | <= 0,020 | <= 0,020 | <= 0,30 | >= 0,020 | 10 - 50 | 630 | 540 |
| 1.5526 | - | - | 30MNB4 | C30BCR | 0,27 - 0,32 | 0,80 - 1,10 | <= 0,15 | <= 0,020 | <= 0,020 | 0,10 - 0,30 | >= 0,020 | 10 - 50 | 630 | 540 |
| 1.5511 | - | 35B2 | - | C35B | 0,32 - 0,38 | 0,60 - 0,90 | <= 0,15 | <= 0,020 | <= 0,020 | <= 0,30 | >= 0,020 | 10 - 50 | 680 | 600 |
| 1.5511 | - | 35B2 | - | C35BCR | 0,32 - 0,38 | 0,60 - 0,90 | <= 0,15 | <= 0,020 | <= 0,020 | 0,10 - 0,30 | >= 0,020 | 10 - 50 | 720 | 610 |
| 1.5537 | - | - | 36MNB4 | C35B2 | 0,33 - 0,38 | 0,80 - 1,10 | <= 0,15 | <= 0,020 | <= 0,020 | <= 0,30 | >= 0,020 | 10 - 50 | 730 | 610 |
| 1.5537 | - | - | 36MNB4 | C35BCR1 | 0,33 - 0,38 | 0,80 - 1,10 | <= 0,15 | <= 0,020 | <= 0,020 | 0,10 - 0,30 | >= 0,020 | 10 - 50 | 739 | 610 |
| 1.5538 | 37MNB5 | - | 37MNB5 | C40MNB | 0,35 - 0,40 | 0,15 - 1,45 | <= 0,15 | <= 0,020 | <= 0,020 | <= 0,30 | - | - | - | - |
| GSW Standard specification. Individual variation in any element can be considered. | ||||||||||||||
| W.Nr | DIN Std Des. | Other Des. | EN 10263 - 4:2002 Std Des. | GSW Des. | %C | %Mn | %Si | %P | %S | %Cr | %Mo | %Al | B (ppm) | Rmax annealed conditions N/mm2 |
|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|
| 1.5408 | 30MOB1 | - | 30MOB1 | C30BCRMO | 0,28 - 0,32 | 0,80 - 1,00 | <= 0,25 | <= 0,025 | <= 0,025 | <= 0,30 | 0,80 - 0,12 | >= 0,020 | 8 - 50 | - |
| 1.7076 | - | - | 32CRB4 | C32CRB4 | 0,30 - 0,34 | 0,60 - 0,90 | <= 0,25 | <= 0,025 | <= 0,025 | 0,90 - 1,20 | - | >= 0,020 | 10 - 50 | 550 |
| 1.7077 | - | - | 36CRB4 | C36CRB4 | 0,34 - 0,38 | 0,70 - 1,00 | <= 0,25 | <= 0,025 | <= 0,025 | 0,90 - 1,20 | - | >= 0,020 | 10 - 50 | 570 |
| 1.7033 | 34CR4 | ASTM A752 | 34CR4 | C34CR4 | 0,30 - 0,37 | 0,60 - 0,90 | <= 0,25 | <= 0,025 | <= 0,025 | 0,90 - 1,20 | - | >= 0,020 | - | 580 |
| 1.7034 | 37CR4 | ASTM A752 | 37CR4 | C37CR4 | 0,34 - 0,41 | 0,60 - 0,90 | <= 0,25 | <= 0,025 | <= 0,025 | 0,90 - 1,20 | - | >= 0,020 | - | 590 |
| 1.7220 | 34CRMO4 | - | 34CRMO4 | C34CRMO4 | 0,30 - 0,37 | 0,60 - 0,90 | <= 0,25 | <= 0,025 | <= 0,025 | 0,90 - 1,20 | 0,15 - 0,30 | >= 0,020 | - | 600 |
| 1.7202 | 37CRMO4 | - | 37CRMO4 | C37CRMO4 | 0,35 - 0,40 | 0,60 - 0,90 | <= 0,25 | <= 0,025 | <= 0,025 | 0,90 - 1,20 | 0,15 - 0,30 | >= 0,020 | - | 620 |
| 1.7035 | 41CR4 | - | 41CR4 | C41CR4 | 0,38 - 0,45 | 0,60 - 0,90 | <= 0,25 | <= 0,025 | <= 0,025 | 0,90 - 1,20 | - | >= 0,020 | - | 610 |
| 1.7039 | 41CRS4 | - | 41CRS4 | C41CRS4 | 0,38 - 0,45 | 0,60 - 0,90 | <= 0,25 | <= 0,025 | 0,020 - 0,040 | 0,90 - 1,20 | - | >= 0,005 | - | 600 |
| 1.7225 | 42CRMO4 | - | 42CRMO4 | C42CRMO4 | 0,38 - 0,45 | 0,60 - 0,90 | <= 0,25 | <= 0,025 | <= 0,025 | 0,90 - 1,20 | 0,15 - 0,30 | >= 0,020 | - | - |
| GSW Standard specification. Individual variation in any element can be considered. | ||||||||||||||